Catalyst composition for the synthesis of multi-walled carbon nanotubes

ABSTRACT

The present invention relates to a catalyst composition for the synthesis of multi-walled carbon nanotube having high apparent density in a manner of high yield. More particularly, this invention relates to a multi-component metal catalyst composition comprising i) main catalyst of Fe and Mo, ii) inactive support of Al and iii) optional co-catalyst at least one selected from Co, Ni, Ti, Mn, W, Sn or Cu. Further, the present invention affords multi-walled carbon nanotube having 5˜15 nm of fibrous diameter and 0.5˜4 μm bundle diameter.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a catalyst composition for thesynthesis of multi-walled carbon nanotube having high apparent densityin a manner of high yield. More particularly, this invention relates toa multi-component metal catalyst composition comprising i) main catalystof Fe and Mo, ii) inactive support of Al and iii) optional co-catalystat least one selected from Co, Ni, Ti, Mn, W, Sn or Cu. Further, thepresent invention affords multi-walled carbon nanotube having 5˜15 nm offibrous diameter and 0.5˜4 μm bundle diameter.

2. Description of Prior Art

Carbon nanotube has a hexagonal honey comb shape in which one carbonatom is bonded with 3 adjacent carbon atoms. Further, the graphite planeis rolled in a round shape having nano size diameter. Specific physicalproperties are shown according to the size and shape of carbon nanotube.The weight of carbon nanotube is comparatively light due to its hollowstructure. Further, the electrical conductivity is as good as that ofcopper, as well as the thermal conductivity is as good as that ofdiamond. Of course, the tensile strength is not less than that of iron.Carbon nonotube can be classified as single walled carbon nanotube,double walled carbon nanotube, multi-walled carbon nanotube and ropecarbon nanotube depending on its rolled shape.

Such carbon nanotube can be generally manufactured by an arc-dischargemethod, a laser vaporization method, a plasma enhanced chemical vapordeposition method, a thermal chemical vapor deposition method, a vaporphase growth method, or an electrolysis method. Among them, a thermalchemical vapor deposition method has been preferably used, because thegrowth of carbon nanotube can be made by the direct reaction betweencarbon source gas and metal catalyst without using the substrate.Further, high purity of carbon nanotube can be economically manufacturedin a large amount according to a thermal chemical vapor depositionmethod.

In a thermal chemical vapor deposition method, the metal catalyst isnecessarily required. Among the metals, Ni, Co, or Fe has been commonlyused. Each particle of metal catalysts can act as seed for the formationof carbon nanotube. Therefore, the metal catalyst has been required tobe formed as nano size particle. Of course, many researches fordeveloping metal catalyst have been tried.

As a metal catalyst preparation method developed up to now, thefollowing preparation methods have been disclosed. First, it has beendisclosed that the method comprises i) preparing the solution containingcatalytic metals and support, ii) co-precipitating the catalystcomposition by adjusting pH, temperature, and/or amount of ingredients,and iii) heat treating the precipitates under air or other gasatmosphere. Second, the method by drying or evaporating the suspensioncontaining catalytic metal and fine grain support has been disclosed.Third, it has been disclosed that the method comprises i) ionizing themetal by mixing catalytic metal salt with cation particle support suchas zeolite, and ii) reducing the ionized metal into metal particle byhydrogen or other reducing agent at high temperature. Fourth, the methodby calcinating catalytic metal with solid oxide support material, suchas, magnesia, alumina, and/or silica has been disclosed. Finally, themethod of calcination for a metal composition has been disclosed wherespray-drying of the catalytic metal precursor solution has beenperformed before calcination.

According to a catalytic chemical vapor deposition method, the metalcatalytic components are slowly consumed in the process of synthesizingcarbon nanotube. This consumption of metal catalytic components iscaused by the inactivation of metal components by encapsulation, wherecarbon atoms encapsulate metal catalytic particles. Generally,re-activation of inactivated catalytic metal is neither possible, noreconomical. In some cases, only few grams of carbon nanotube can beobtained using 1 gram of a metal catalyst composition including metalcatalyst and support material. Therefore, the development of a highlyactive metal catalyst composition and of synthetic conditions has beenrequired in order to produce the carbon nanotube in a commerciallyavailable scale

Following technologies have been reported in patent disclosures orreferences until now.

According to U.S. Pat. No. 5,165,909 by Hyperion Catalysis InternationalInc., a method for producing carbon fibrils which comprises i)calcinating a catalyst composition at about 500° C. under air atmosphereafter Fe catalyst is supported by Al₂O₃, ii) reducing the catalystcomposition using hydrogen gas at about 900° C., and iii) preparingcarbon fibrils by reacting benzene as a carbon source under hydrogenatmosphere at about 1,000° C. has been disclosed. However, the catalyticyield for preparing carbon fibril is not so good. Further, the processfor preparing metal catalyst requires complicate steps of calcinationand reduction as well as more than 800° C. of high reaction temperature.

To overcome such drawbacks of above patent disclosure, U.S. Pat. No.6,696,387 disclosed the catalyst composition comprising i) Fe as maincatalyst, ii) alumina and/or magnesia particle as catalyst support andiii) at least one optional co-catalyst selected from V, Nb, Ta, Cr, Mo,W, Mn, Tc, Re, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, or the lanthanides.However, it is hard to obtain a precise multi-walled carbon nanotubewith a high catalytic yield using this catalyst composition, because theuniformed dispersion between metal catalyst and support material cannotbe accomplished due to the use of alumina and/or magnesia supportmaterial.

In PCT publication No. WO 2007/33438, a catalyst system for multi-walledcarbon nanotube production has been disclosed. In this disclosure, acatalyst system for the selective conversion of hydrocarbons intomulti-walled carbon nanotubes and hydrogen comprising a compound of theformula: (Ni, Co)Fe_(y)O_(z)(Al₂O₃)_(w) has been disclosed. Further, aspreferred catalyst compositions, CoFe₂O₄(Al₂O₃)_(4.5), CoFe₂O₄(Al₂O₃)₁₆,and CoFe₂O₄ (Al₂O₃)₃₂ have been disclosed. Therefore, the catalystcomposition comprising i) (Ni, Co) and Fe as main catalyst and ii)alumina as catalyst support has been disclosed. However, it is also hardto obtain a precise multi-walled carbon nanotube with a high catalyticyield using this catalyst composition, because the uniformed dispersionbetween metal catalyst and support material cannot be accomplished dueto the use of alumina support material.

To overcome the low catalytic yield caused by non-uniformed dispersionof a catalyst composition, the inventors of present application havefirstly disclosed a catalyst composition under U.S. Pat. No. 8,048,821‘Catalyst composition for the synthesis of thin multi-walled carbonnanotube and its manufacturing method’.

In this U.S. Pat. No. 8,048,821, a catalyst composition for producingcarbon nanotube represented by following formula[Fe_(a):Al_(b)]_(x):M_(y):Mg_(z) has been disclosed. In this formula, Ferepresents catalytic metal of iron, its oxide, or its derivative; Alrepresents catalytic metal of aluminum, its oxide, or its derivative; Mgrepresents inactive support of magnesium, its oxide, or its derivative;and M represents at least one transition metal selected from Co, Ni, Cr,Mn, Mo, W, V, Sn, or Cu, its oxide or its derivative.

On the other hand, the inventors of present application have furtherdisclosed a catalyst composition under U.S. Pat. Application publicationNo. US 2012/0077031 A1 ‘Catalyst composition for the synthesis of thinmulti-walled carbon nanotube’.

In this U.S. Pat. Application publication No. US 2012/0077031 A1, acatalyst composition for producing carbon nanotube represented byfollowing formula [Co_(a):Al_(b)]_(x):M_(y):Mg_(z) has been disclosed.In this formula, Co represents catalytic metal of cobalt, its oxide, orits derivative; Al represents catalytic metal of aluminum, its oxide, orits derivative; Mg represents inactive support of magnesium, its oxide,or its derivative; and M represents at least one transition metalselected from Ni, Cr, Mn, Mo, W, Pb, Ti, Sn, or Cu, its oxide, or itsderivative.

Even though our previous catalyst composition represented by formula of[Fe_(a):Al_(b)]_(x):M_(y):Mg_(z) or [Co_(a):Al_(b)]_(x):M_(y):Mg_(z) hasadopted Mg as inactive support, Mg cannot make a sufficient role ofinactive support in case that Mg is mixed with other metal catalystcomponents. Therefore, our previous catalyst composition may have ahandicap of synthesizing multi-walled carbon nanotubes having highdensity in a sufficiently high yield.

Therefore, the inventors of present application have developed novelcatalyst composition by replacing the inactive support from Mg to Al, oncondition that Fe and Mo have been adopted as main catalytic components.Further, since all catalytic components containing inactive supportmaterial in the present application have been prepared usingspray-drying, spray pyrolysis, or co-precipitation process in theaqueous solution, the catalyst composition can be obtained as highlyuniformed and dispersed fine powder form. Preferably, the catalystcomposition would be better to be prepared using co-precipitationprocess in order to obtain the most uniformed and dispersed fine powderform.

Further, in the course of preparing a catalyst composition, a hydrogenreduction step has not been introduced.

Finally, the inventors of present application have developed amulti-component metal catalyst composition comprising i) main catalystof Fe and Mo, ii) inactive support of Al and iii) optional co-catalystat least one selected from Co, Ni, Ti, Mn, W, Sn, or Cu. Further, thepresent invention affords multi-walled carbon nanotube having 5˜15 nm offibrous diameter and 0.5˜4 μm bundle diameter.

SUMMARY OF THE INVENTION

The object of present invention is to provide a catalyst composition forproducing carbon nanotube represented by following formula.[Fe_(a):Mo_(b)]_(x):M_(y):Al_(z)

wherein

Fe, Mo represents catalyst active material of iron, molybdenum, itsoxide, or its derivative; Al represents inactive support material ofaluminum, its oxide, or its derivative;

M represents at least one transition metal selected from Co, Ni, Ti, Mn,W, Sn, or Cu, its oxide, or its derivative.

x, y, and z represent molar fraction of [the sum of Fe and Mo], M andAl,

x+y+z=10, 1.0≦x≦4.0, 0.1≦y≦3.0, 2.5≦z≦8.0;

a and b represent molar fraction of Fe and Mo,

a+b=10, 7.9≦a≦9.9, 0.1≦b≦2.1.

Further, the molar fraction of [the sum of Fe and Mo], M, and Al ispreferably x+y+z=10, 1.5≦x≦3.5, 0.3≦y≦2.5, 3.0≦z≦7.5;

a and b represent molar fraction of Fe and Mo,

a+b=10, 7.7≦a≦9.7, 0.3≦b≦2.3.

Further, the molar fraction of [the sum of Fe and Mo], M, and Al is morepreferably x+y+z=10, 2.0≦x≦3.0, 0.6≦y≦2.0, 3.5≦z≦7.0;

a and b represent molar fraction of Fe and Mo,

a+b=10, 7.5≦a≦9.5, 0.5≦b≦2.5.

The other object of the present invention is to provide a process forpreparing a catalyst composition for synthesizing carbon nanotubecomprising i) dissolving multi-component metal salts for the metalcatalyst composition ([Fe_(a):Mo_(b)]_(x):M_(y):Al_(z)) comprisingcatalyst active metal (Fe and Mo), inactive support (Al) and transitionmetal (M) in water; ii) co-precipitating a multi-component catalystcomposition by adding co-precipitating agent solution, spray-drying thesolution containing the multi component metal salt, or spray pyrolysisof the solution containing the multi component metal salt; iii)filtering, drying, and milling the obtained co-precipitated catalystcomposition; iv) calcinating the milled catalyst composition by thermaloxidation at 400˜1,200° C.; and v) dried-milling and grinding thecalcinated catalyst composition after thermal oxidation.

As metal salt, the form of nitrate, sulfate, acetate, alkoxide,carbonate, or chloride is preferred.

On the other hand, the further object of the present invention is toprovide a process for preparing carbon nanotube having high apparentdensity comprising i) preparing a catalyst composition for the synthesisof carbon nanotube; ii) supplying mixed gas of hydrogen and at least onecarbon source selected from saturated or unsaturated hydrocarbon having1˜4 carbon atoms to the reactor at 500˜900° C.; and iii) growing andsynthesizing carbon nanotube by thermal decomposition of supplied carbonsource on the surface of a catalyst composition according to a thermalchemical vapor deposition method.

As reactor, vertical fixed-bed reactor, horizontal fixed-bed reactor,rotary kiln reactor, moving bed reactor, or fluidized bed reactor can beused.

According to the method for preparing carbon nanotube, multi-walledcarbon nanotube having 5˜15 nm of fibrous diameter and 0.5˜4 μm bundlediameter can be prepared.

The further object of present invention is to provide a method for usingmulti-walled carbon nanotube as electrically conductive and strengthenhanced fillers in polymer composite material, thermal conductive andstrength enhanced fillers in metal composite, catalyst support of fuelcell, support material of organic process catalyst, storage material formethane and hydrogen gas, electrode material of lithium secondarybattery, conductive material of lithium secondary battery, electrodematerial for high capacity electric double layer capacitor, fieldemitting material for display, and membrane material.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a FE-SEM (Field Emission Scanning Electron Microscope)photograph of carbon nanotube prepared in Example 1 of presentapplication.

FIG. 2 shows a Raman graph of carbon nanotube prepared in Example 1 ofpresent application.

FIG. 3 shows a TGA (Thermogravimetric Analysis) graph of carbon nanotubeprepared in Example 1 of present application.

DETAILED DESCRIPTION OF THE INVENTION

Present invention relates to a catalyst composition for producing carbonnanotube represented by following formula.[Fe_(a):Mo_(b)]_(x):M_(y):Al_(z)

wherein

Fe, Mo represents catalyst active material of iron, molybdenum, itsoxide, or its derivative; Al represents inactive support material ofaluminum, its oxide, or its derivative;

M represents at least one transition metal selected from Co, Ni, Ti, Mn,W, Sn, or Cu, its oxide, or its derivative.

x, y, and z represent molar fraction of [the sum of Fe and Mo], M andAl,

x+y+z=10, 1.0≦x≦4.0, 0.1≦y≦3.0, 2.5≦z≦8.0;

a and b represent molar fraction of Fe and Mo,

a+b=10, 7.9≦a≦9.9, 0.1≦b≦2.1.

Further, the molar fraction of [the sum of Fe and Mo], M, and Al ispreferably x+y+z=10, 1.5≦x≦3.5, 0.3≦y≦2.5, 3.0≦z≦7.5;

a and b represent molar fraction of Fe and Mo,

a+b=10, 7.7≦a≦9.7, 0.3≦b≦2.3.

Further, the molar fraction of [the sum of Fe and Mo], M, and Al is morepreferably x+y+z=10, 2.0≦x≦3.0, 0.6≦y≦2.0, 3.5≦z≦7.0;

a and b represent molar fraction of Fe and Mo,

a+b=10, 7.5≦a≦9.5, 0.5≦b≦2.5.

One of characteristics of the catalyst composition of present inventionis to provide a uniformly dispersed catalyst composition comprising i)main catalyst of Fe and Mo, ii) inactive support of Al and iii) optionalco-catalyst at least one selected from Co, Ni, Ti, Mn, W, Sn, or Cu. Thecatalyst composition can be prepared by i) co-precipitating amulti-component catalyst composition by adding co-precipitating agentsolution, ii) spray-drying the solution containing the multi componentmetal salt, or iii) spray pyrolysis of the solution containing the multicomponent metal salt.

The other object of the present invention is to provide a process forpreparing a catalyst composition for synthesizing carbon nanotubecomprising i) dissolving multi-component metal salts for the catalystcomposition ([Fe_(a):Mo_(b)]_(x):M_(y):Al_(z)) in water; ii)co-precipitating a multi-component catalyst composition by addingco-precipitating agent solution, spray-drying the solution containingthe multi component metal salt, or spray pyrolysis of the solutioncontaining the multi component metal salt; iii) filtering and drying theobtained precipitated catalyst composition at 80˜230° C. in the oven;iv) milling the dried catalyst composition; v) calcinating the milledcatalyst composition by thermal oxidation at 400˜1,200° C.; and vi)dried-grinding the calcinated catalyst composition after thermaloxidation.

As metal salt, the form of nitrate, sulfate, acetate, alkoxide,carbonate, or chloride is preferred. Nitrate can be preferably used asmetal salt.

For the preparation of carbon nanotube, the calcinated catalystcomposition can be placed in the vertical or horizontal fixed-bed quartzfurnace. Then, saturated or unsaturated hydrocarbon gas having 1˜4carbon atoms is supplied at 500˜900° C. Carbon nanotube can be preparedon the surface of catalyst in a high yield. Various kinds of reactor canbe used for preparing carbon nanotube. For example, vertical fixed-bedreactor, horizontal fixed-bed reactor, rotary kiln reactor, mobile bedreactor, or fluidized bed reactor can be used.

In a preparation method of carbon nanotube, the supply of a catalystcomposition and the recovery of carbon nanotube can be carried out in acontinuous or discontinuous process. For the synthesis of carbonnanotube, carbon source gas, such as, methane, ethane, propane, butane,ethylene, propylene, butene, or butadiene has to be supplied. Of course,hydrogen gas or inert gas can be supplied together with carbon sourcegas. The reaction can be performed under the pressure of 0.1˜2 bar aswell as at the temperature of 500˜900° C. However, the reactionconditions have to be controlled to make a deposition of carbon in anappropriate rate without auto-decomposition of gas phase hydrocarbon.The preferred reaction temperature is 500˜800° C.

The form of calcinated powder is preferred. After finishing synthesis ofcarbon nanotube, catalyst component in the carbon nanotube can beremoved by a physical or a chemical method. For this purpose, theobtained carbon nanotube can be treated with acid or base as well asheat treatment at high temperature.

According to the preparation method of present invention, carbonnanotube having 5˜15 nm of diameter can be prepared in the 3˜5 timeshigher yields than the conventional method. Further, additional removalof catalyst in the carbon nanotube may not be required, because theobtained carbon nanotube of present invention shows very low level ofremaining catalyst components in the carbon nanotube. However, theobtained carbon nanotube can be physically or chemically treated forintroducing a functional group to the surface of carbon nanotube orburning impure carbon materials.

The obtained carbon nanotube of present invention can be used aselectrical conductive and strength enhanced fillers in polymer compositematerial, thermal conductive and strength enhanced fillers in metalcomposite, catalyst support of fuel cell, support material of organicprocess catalyst, storage material for methane and hydrogen gas,electrode material of lithium secondary battery, conductive material oflithium secondary battery, electrode material for high capacity electricdouble layer capacitor, field emitting material for display, andmembrane material.

The outstanding advantageous effect of present invention is to provide amulti-walled carbon nanotube having 5˜15 nm of fibrous diameter, 0.5˜4μm bundle diameter and 100˜10,000 of aspect ratio in a high yield.Further, the catalyst composition of present invention comprising i)main catalyst of Fe and Mo, ii) inactive support of Al and iii) optionalco-catalyst at least one selected from Co, Ni, Ti, Mn, W, Sn or Cu, thusenabling to prepare high purity multi-walled carbon nanotube in 3˜5times higher yields than the conventional method in a short period, suchas, 30 minutes.

Further, the other outstanding advantageous effect of present inventionis to provide a simple process for preparing a catalyst composition,wherein a hydrogen reduction step has not been introduced. Due to thesimple preparation step of a catalyst composition and high catalyticyield of present invention, the production cost of carbon nanotube canbe reduced. Further, the reduced cost for producing carbon nanotubeaffords that carbon nanotube can be applied in various fields in aneconomical manner.

The present invention can be explained more concretely by followingExamples and Comparative Examples. However, the scope of the presentinvention shall not be limited by following Examples.

EXAMPLES Example 1 Preparation of a Catalyst Composition with aVariation of the Molar Amount of Fe and Mo

The carbon nanotube using catalyst composition consisting of Fe, Mo, andAl with Ni among metal M has been prepared. The molar ratio of Fe and Mois changed from 10:0 to 0:10 wherein the molar ratio of Fe+Mo is fixedas 3, the molar ratio of M is fixed as 0.5, the molar ratio of Al isfixed as 6.5. After preparing a catalyst composition with a variation ofthe molar amount of Fe and Mo, carbon nanotubes have been prepared usingthese catalyst compositions. Catalytic yields have been measured foreach of catalyst compositions.

The catalyst composition has been prepared as following methods. Thesolution containing a selected amount of Fe(NO₃)₃.9H₂O,(NH₄)₆Mo₇O₂₄.4H₂O, Al(NO₃)₃.9H₂O, and Ni(NO₃)₂.6H₂O in de-ionized waterhas been prepared. And then crystal form of catalyst composition isprepared by spray pyrolysis of the solution containing the multicomponent metal salt at 750° C.

Carbon nanotube has been prepared using the obtained catalystcomposition in fixed bed reactor in an experimental scale. A selectedamount of a catalyst composition has been placed at the mid part ofquartz furnace reactor. The reactor has been heated to the desiredtemperature under nitrogen atmosphere. Mixed gas of ethylene andnitrogen gas in a volume ratio of 3:1 has been supplied and flowed forthe synthesis of carbon nanotube. After 1 hour of synthesis, an amountof multi-walled carbon nanotube has been prepared. The amount of carbonnanotube has been measured at room temperature. The structure and shapeof carbon nanotube have been analyzed using FE-SEM analyses.

The catalytic yield has been measured by following equation. Catalyticyield=100×(M_(total)−M_(cat))/(M_(cat)), apparent density=the carbonnanotube weight (g) in container/volume of container (cc). Table 1 andTable 2 show the results of carbon nanotube synthesis using the catalystcomposition prepared in Example 1.

As shown in Table 1, carbon nanotube can be prepared in a high yieldwhen the range of molar ratio of Fe and Mo is within Fe 7.9≦a≦9.9 and Mo0.2≦b≦2.1 in case of a+b=10.

TABLE 1 The synthesis of carbon nanotube using the catalyst compositionprepared in Example 1. Catalyst Reaction amount of Reaction CatalyticApparent amount temp. reaction gas time yield density catalystcomposition (mg) (° C.) (mL/minutes) (minutes) (%) (g/cc) [Fe:Mo]:Ni:Al= 100 700 C₂H₄:N₂ = 30:13 60 1,274 0.020 [9.86:0.14]:0.5:6.5[Fe:Mo]:Ni:Al = 1,384 0.022 [9.58:0.42]:0.5:6.5 [Fe:Mo]:Ni:Al = 1,4230.025 [9.28:0.72]:0.5:6.5 [Fe:Mo]:Ni:Al = 1,397 0.028[8.97:1.03]:0.5:6.5 [Fe:Mo]:Ni:Al = 1,372 0.030 [8.65:1.35]:0.5:6.5[Fe:Mo]:Ni:Al = 1,346 0.037 [8.31:1.69]:0.5:6.5 [Fe:Mo]:Ni:Al = 1,2920.043 [7.96:2.04]:0.5:6.5Remarks: The molar ratio of [Fe:Mo]:Ni:Al is constantly fixed as3.0:0.5:6.5 in all catalyst compositions.

Comparative Example 1 Preparation of a Catalyst Composition with aVariation of the Molar Amount of Fe and Mo

After preparing a catalyst composition with a variation of the molaramount of Fe and Mo, carbon nanotubes have been prepared using thesecatalyst compositions. Catalytic yields have been measured for each ofcatalyst compositions.

Other conditions for preparing a catalyst composition are same as thoseshown in Example 1. Further, the conditions for preparing carbonnanotube are also same as those shown in Example 1. Of course, acatalytic yield has been measured using the same manner in Example 1.

Table 2 shows the results of carbon nanotube synthesis using thecatalyst composition prepared in Comparative Example 1. As shown inTable 2, when the range of molar ratio of Fe and Mo deviates from Fe7.9≦a≦9.9 and Mo 0.1≦b≦2.1 in case of a+b=10, carbon nanotube cannot beprepared in a high yield, even though the apparent density of carbonnanotube increases.

Further, in the case that Mo is not included in a catalyst composition,that is, Fe:Ni:Al=3:0.5:6.5, the apparent density cannot be satisfied,even though catalytic yield of carbon nanotube is excellent. Therefore,not a little dust has been generated in the course of preparing carbonnanotube due to its low apparent density. As a conclusion, carbonnanotube having high apparent density cannot be prepared using only Feas main catalytic metal, while carbon nanotube having high apparentdensity can be prepared in a high yield using Fe and Mo as maincatalytic metals.

TABLE 2 The synthesis of carbon nanotube using the catalyst compositionprepared in Comparative Example 1. Catalyst Reaction amount of ReactionCatalytic Apparent amount temp. reaction gas time yield density Catalystcomposition (mg) (° C.) (mL/minutes) (minutes) (%) (g/cc) [Fe:Mo]:Ni:Al= 100 700 C₂H₄:N₂ = 30:13 60 1,352 0.008 [10:0]:0.5:6.5 [Fe:Mo]:Ni:Al =1,154 0.034 [4.31:5.69]:0.5:6.5 [Fe:Mo]:Ni:Al = 772 0.048[3.16:7.84]:0.5:6.5 [Fe:Mo]:Ni:Al = 386 0.057 [1.86:8.14]:0.5:6.5[Fe:Mo]:Ni:Al = 117 0.07 [0:10]:0.5:6.5

Remarks: The molar ratio of [Fe:Mo]:Ni:Al is constantly fixed as3.0:0.5:6.5 in all catalyst compositions.

Example 2 Catalyst Compositions for Preparing Carbon Nanotube

A catalyst composition comprising Fe, Mo, Al and metal M has beenprepared for the synthesis of carbon nanotube. The molar fraction of[Fe+Mo], M, and Al is 2:1:7 and the molar fraction of Fe and Mo is9.28:0.72. Further, various kinds of transition metal (M) has been usedfor catalyst compositions. The catalytic yield for each catalystcomposition has been measured after preparation of carbon nanotube.

The catalyst composition has been prepared as following methods. Thesolution dissolved with a selected amount of Fe(NO₃)₃.9H₂O,(NH₄)₆Mo₇O₂₄.4H₂O, Al(NO₃)₃.9H₂O and one kind of metal salt selectedfrom Co(No₃)₂.6H₂O, Cu(NO₃)₂.3H₂O, Mn(NO₃)₄.4H₂O, (NH₄)₁₀W₁₂O₄₀.5H₂O,TiCl₃, or SnCl₄.5H₂O in de-ionized water has been prepared. Then,crystal form of catalyst composition is prepared after spray pyrolysisof the solution containing the multi component metal salt at 750° C.

Carbon nanotube has been prepared using the obtained catalystcomposition in fixed bed reactor in an experimental scale. A selectedamount of a catalyst composition has been placed at the mid part ofquartz furnace reactor. The reactor has been heated to the desiredtemperature under nitrogen atmosphere. Mixed gas of ethylene andnitrogen gas in a volume ratio of 3:1 has been supplied and flowed forthe synthesis of carbon nanotube. After 1 hour of synthesis, an amountof multi-walled carbon nanotube has been prepared. The amount of carbonnanotube has been measured at room temperature. The structure and shapeof carbon nanotube have been analyzed using FE-SEM analyses.

The catalytic yield has been measured by following equation. Catalyticyield=100×(M_(total)−M_(cat))/(M_(cat)), apparent density=the carbonnanotube weight (g) in container/volume of container (cc). Table 3 showsthe results of carbon nanotube synthesis using the catalyst compositionprepared in Example 2.

Even though a catalyst composition, comprising Fe, Mo, Al, metal M whensatisfying the range of selected molar fraction ratio, shows highcatalytic yield as shown in Example 1, the catalytic yield of presentcatalyst composition can be much enhanced when selected amount of M isadded in the catalyst composition as shown in Table 3. Further, carbonnanotube having high apparent density can be prepared using the catalystcomposition prepared in Example 2 in case that other carbon source, suchas, propane can be used instead of ethylene

TABLE 3 The synthesis of carbon nanotube using the catalyst compositionprepared in Example 2. Catalyst Reaction amount of Reaction CatalyticApparent amount temp. reaction gas time yield density catalystcomposition (mg) (° C.) (mL/minutes) (minutes) (%) (g/cc) [Fe:Mo]:Ni:Al= 100 700 C₂H₄:N₂ = 30:13 60 1,542 0.025 [9.28:0.72]:1:7 [Fe:Mo]:Co:Al =1,543 0.022 [9.28:0.72]:1:7 [Fe:Mo]:Mn:Al = 1,526 0.017 [9.28:0.72]:1:7[Fe:Mo]:Cu:Al = 1,519 0.019 [9.28:0.72]:1:7 [Fe:Mo]:W:Al = 1,423 0.020[9.28:0.72]:1:7 [Fe:Mo]:Ti:Al = 1,503 0.019 [9.28:0.72]:1:7[Fe:Mo]:Sn:Al = 1,487 0.021 [9.28:0.72]:1:7Remarks: The molar ratio of [Fe:Mo]:metal M:Al is constantly fixed as2:1:7 in all catalyst compositions.

Comparative Example 2 Catalyst Compositions for Preparing CarbonNanotube

Further, we have also prepared a catalyst composition that does notcontain metal M component, or that contains an excess or a deficientamount of transition metal M in order to see the dependence of thecatalytic yield on the amount of metal M.

Table 4 shows the results of carbon nanotube synthesis using thecatalyst composition prepared in Comparative Example 2. As shown inTable 4, when the range of molar ratio of metal M deviates from0.1≦y≦3.0, carbon nanotube cannot be prepared in a high yield as well asa high apparent density.

Further, in the case that M is not included in a catalyst composition,that is, [Fe:Mo]:metal M:Al=3:0:7, both apparent density and highcatalytic yield cannot be accomplished. As a conclusion, we estimatethat metal M can be act as co-catalyst for enhancing both catalyticyield and apparent density of carbon nanotube.

TABLE 4 The synthesis of carbon nanotube using the catalyst compositionprepared in Comparative Example 2. Catalyst Reaction amount of ReactionCatalytic Apparent amount temp. reaction gas time yield density Catalystcomposition (mg) (° C.) (mL/minutes) (minutes) (%) (g/cc) [Fe:Mo]:Ni:Al= 100 700 C₂H₄:N₂ = 30:13 60 1,063 0.048 [9.28:0.72]:5:3 [Fe:Mo]:Ni:Al =1,147 0.037 [9.28:0.72]:4:4 [Fe:Mo]:Ni:Al = 1,162 0.012[9.28:0.72]:0.05:7.95 [Fe:Mo]:Ni:Al = 959 0.01 [9.28:0.72]:0.025:7.975[Fe:Mo]:Al = 845 0.009 [9.28:0.72]:8

What is claimed is:
 1. A catalyst composition for producing carbonnanotube represented by the following formula:[Fe_(a):Mo_(b)]_(x):M_(y):Al_(z) wherein Fe, Mo represents catalystactive material of iron, molybdenum, its oxide, or its derivative; Alrepresents inactive support material of aluminum, its oxide, or itsderivative; M represents at least one transition metal selected from thegroup consisting of Co, Ni, Ti, Mn, W, Sn, Cu, and oxides, orderivatives thereof; x, y, and z represent molar fraction of [the sum ofFe and Mo], M and Al, x+y+z=10 , 1.0≦x≦4.0, 0.1≦y≦3.0, 2.5≦z≦8.0; and aand b represent molar fraction of Fe and Mo, a+b=10, 7.9≦a≦9.9, 0.1≦b≦2.1.
 2. The catalyst composition for producing carbon nanotubeaccording to claim 1, wherein the molar fraction of [the sum of Fe andMo], M, and Al is x+y+z=10, 3.0z7.5; a and b represent molar fraction ofFe and Mo, a+b=10, 7.7≦a≦9.7 , 0.3≦b≦2.3.
 3. The catalyst compositionfor producing carbon nanotube according to claim 2, wherein the molarfraction of [the sum of Fe and Mo], M, and Al is x+y+z=10, 2.0≦x≦3.0,0.6≦y≦2.0, 3.5≦z≦7.0; a and b represent molar fraction of Fe and Mo,a+b=10, 7.0≦a≦9.5, 0.5≦b≦2.5.
 4. A process for preparing a catalystcomposition for synthesizing carbon nanotube of claim 1 comprising: i)dissolving multi-component metal salts for the metal catalystcomposition ([Fe_(a):Mo_(b]) _(x):M_(y):Al_(z)) comprising catalystactive metal(Fe and Mo), inactive support(Al) and transition metal(M) inwater; ii) co-precipitating a multi-component catalyst composition byadding co-precipitating agent solution, spray-drying the solutioncontaining the multi-component metal salt, or spray pyrolysis of thesolution containing the multi-component metal salt; iii) filtering,drying, and milling the obtained co-precipitated catalyst composition;iv) calcinating the milled catalyst composition by thermal oxidation at400⁻1,200° C; and v) dried-milling and grinding the calcinated catalystcomposition after thermal oxidation.
 5. The process for preparing acatalyst composition for synthesizing carbon nanotube according to claim4, wherein the multi-component metal salts are in the form of nitrate,sulfate, acetate, alkoxide, carbonate, or chloride.